MgO Board

MgO Board otherwise called “Magnesium Oxide Board”  is a factory-made product. It is a type of relatively new inorganic-bonded composite. Its main mineral being Magnesium Oxide (MgO). MgO Boards are produced with alkali–resistant fiberglass mesh as strengthening material. Magnesium oxide (melting point of 2,800°C) is often used as a basic refractory material for lining crucibles & furnaces.

Dimensions

Length (mm)		Width (mm)		Thickness Range (mm)
2440	1220		3mm – 25mm

MgO Board Properties

Density Kg/m3 Nominal	950 to 1100 kg/M3
Tensile Strength Mpa Minimum	5Mpa
Bending Strength Mpa Minimum	9Mpa-16Mpa
Shrink Tolerance Ln mm	±0.5
Specific Absorption Ratio Maximum in %	22%
Moisture Distortion Rate Maximum in %	0.34%
Sustained Combustion Time in %	0%
Length Tolerance in mm	±4
Shock Strength KJ/m2 Minimum	5.5KJ/M2
Thermal Conductivity W/m K Maximum	0.132W/mk
No Asbestos Content
Flatness in mm	2mm
Temperature Shrinkage Rate in % Maximum	0.1%
Fire Redundancy (Non-Combustible A Grade)	A Grade
Minimum Bending strength Mpa	10.5Mpa

Contact Information:

Susan Wei

Beijing Hocreboard Building Materials Co.,Ltd

Tel: 86 15001321220

Fax: 86 62151268

Web: www.hocre-board.com 

Email: info@hocre-board.com 

Skype: susan.wei1

WhatsApp:+8615001321220